Effects of Repeated Wet-Dry Cycles on Compressive Strength of Fly-Ash Based Recycled Aggregate Geopolymer Concrete (RAGC)

Download pdf | Full Screen View

Date Issued:
2018
Abstract/Description:
Geopolymer concrete (GC) is a sustainable construction material and a great alternative to regular concrete. GC is a zero-cement material made from a combination of aluminate, silicate and an activator to produce a binder-like substance. This investigation focused on the effects of wet and dry cycles on the strength and durability of fly ash-based recycled aggregate geopolymer concrete (RAGC). The wet-dry cycles were performed approximately according to ASTM D559 standards. RAGC specimens with nearly 70% recycled materials (recycled aggregate and fly ash) achieved a compressive strength of approximately 3600 psi, after 7 days of heat curing at 60ºC. Although the recycled aggregate is prone to high water absorption, the compressive strength decreased by only 4% after exposure to 21 wet-dry cycles, compared to control specimens that were not exposed to the same conditions. Accordingly, the RAGC material developed in this study can be considered as a promising environmentally friendly alternative to cement-based regular concrete.
Title: Effects of Repeated Wet-Dry Cycles on Compressive Strength of Fly-Ash Based Recycled Aggregate Geopolymer Concrete (RAGC).
81 views
27 downloads
Name(s): Mendelson, Monica, author
Sobhan, Khaled, Thesis advisor
Florida Atlantic University, Degree grantor
College of Engineering and Computer Science
Department of Civil, Environmental and Geomatics Engineering
Type of Resource: text
Genre: Electronic Thesis Or Dissertation
Date Created: 2018
Date Issued: 2018
Publisher: Florida Atlantic University
Place of Publication: Boca Raton, Fla.
Physical Form: application/pdf
Extent: 114 p.
Language(s): English
Abstract/Description: Geopolymer concrete (GC) is a sustainable construction material and a great alternative to regular concrete. GC is a zero-cement material made from a combination of aluminate, silicate and an activator to produce a binder-like substance. This investigation focused on the effects of wet and dry cycles on the strength and durability of fly ash-based recycled aggregate geopolymer concrete (RAGC). The wet-dry cycles were performed approximately according to ASTM D559 standards. RAGC specimens with nearly 70% recycled materials (recycled aggregate and fly ash) achieved a compressive strength of approximately 3600 psi, after 7 days of heat curing at 60ºC. Although the recycled aggregate is prone to high water absorption, the compressive strength decreased by only 4% after exposure to 21 wet-dry cycles, compared to control specimens that were not exposed to the same conditions. Accordingly, the RAGC material developed in this study can be considered as a promising environmentally friendly alternative to cement-based regular concrete.
Identifier: FA00013016 (IID)
Degree granted: Thesis (M.S.)--Florida Atlantic University, 2018.
Collection: FAU Electronic Theses and Dissertations Collection
Note(s): Includes bibliography.
Subject(s): Polymer-impregnated concrete
Recycled materials
Fly ash
Polymers--Compression testing
Held by: Florida Atlantic University Libraries
Sublocation: Digital Library
Persistent Link to This Record: http://purl.flvc.org/fau/fd/FA00013016
Use and Reproduction: Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder.
Use and Reproduction: http://rightsstatements.org/vocab/InC/1.0/
Host Institution: FAU
Is Part of Series: Florida Atlantic University Digital Library Collections.